Above Woods A Vinyl Tiles
TECHNICAL SPECIFICATIONS
Total Thickness: 5.00mm / 3.00mm (Parallelogram)
Wear Layer Thickness: 0.50mm / 0.30mm (Parallelogram)
Tile Size: 100cm*25cm / 11cm*56.57cm (Parallelogram)
Pieces per Box: 8 pcs/box (2m²) /
24 pcs/box (1.488m²) (Parallelogram)
Installation Method: Loose Lay / GlueDown (Parallelogram)
Usage Classification: 42 Light Industrial General / 33 Commercial Heavy
Warranty: Lifetime Limited Commercial Warranty
Slip Resistance: EN13893:2002, DS
Fire Rating: EN13501-1:2007+A1:2009 Bf1-s1
GB8624-2012 B1(B-s1, t0)
Performance: EN ISO 10582: 2012
GB/T 4085-2015
INSTALLATION
PERFORMANCE SPECIFICATIONS
Flammability Tests
Slip resistance Test
Formaldehyde Test
Color Fastness
to artifitial light
Residual indentation
Dimensional stability
after exposure to heat
Curling after exposure
to heat
Effect of castor chair
Composition
Test Code
EN13501
EN13893:2002
EN717-1
ISO 105-B02:2014
Method 3
ISO 24343-1:2007
ISO 23999:2008
ISO 23999:2008
ISO 4918:2016
EN13501
EN13893:2002
EN717-1
ISO 105-B02:2014
Method 3
ISO 24343-1:2007
ISO 23999:2008
ISO 23999:2008
ISO 4918:2016
Standard
Bfl-S1
DS
E1
≥Grade 6
Average value: ≤0.1mm
≤0.25%(tiles intended for dry-joint laying)
≤0.4%(sheets and tiles intended for heat welding)
≤2mm(tiles intended for dry-joint laying)
≤8mm(sheets and tiles intended for heat welding)
After 25,000 cycles, no delamination shall occur.
No disturbance to the surface other
than a slight change in apperance
PVC, DOTP, Calcium Carbonate, Fiber Glass
Bfl-S1
DS
E1
≥Grade 6
Average value: ≤0.1mm
≤0.25%(tiles intended for dry-joint laying)
≤0.4%(sheets and tiles intended for heat welding)
≤2mm(tiles intended for dry-joint laying)
≤8mm(sheets and tiles intended for heat welding)
After 25,000 cycles, no delamination shall occur.
No disturbance to the surface other
than a slight change in apperance
PVC, DOTP, Calcium Carbonate, Fiber Glass
Test Results
Pass
Pass
Pass
Pass
Pass
Pass
Pass
Pass
Pass
Pass
Pass
Pass
Pass
Pass
Pass
Pass